| The maximum temperature: | 300°C |
| Temperature fluctuation: | Within ± 0.5°C |
| Temperature uniformity: | Within ± 1°C |
| Rotate speed of the turntable: | 11 r/min to 12r/min, turntable dimension diameter: 285 mm |
| Vacuum degree: | 0 to 90 KPa |
| Accuracy: | 1 % FS |
| Resolution: | 0.1 KPa |
| Vacuum chamber effective size: | 270 × 210 mm |
| Resolution: | 0.1 % O2 |
| Measuring range: | 0 to 100 % O2 |
| Precision: | ± 0.4 % O2 |
| Response time: | < 10 S |
| Temperature range: | 10 to 35°C |
| Maximum falling height: | 2000 mm |
| Resolution of displacement: | 1 mm |
| Height error: | < ± 2 mm |
| Impact Speed & Energy (charpy): | 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J |
| Impact energy (Izod): | 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J |
| Resolution of impact energy: | 0.001 J |
| Pendulum up angle: | 160° |
| Seal temperature: | Room temperature -250°C |
| Control accuracy: | ± 0.2°C |
| Dwell time: | 0.1 S to 999.9 S |
| Dwell pressure: | 0.05 to 0.7 MPa |
| Standard roller: | 2000 ± 50 g |
| Testing stations: | 3 |
| Dimension (L*W*H) tester: | 320×210×550 mm (3 stations) |
| Weight for stations: | 10 kg (3 stations) |
| Standard roller: | 2000 ± 50 g |
| Testing stations: | 6 |
| Dimension (L*W*H) tester: | 650×210×550 mm (6 stations) |
| Weight for stations: | 15 kg (6 stations) |
| Measuring range: | 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density) |
| Measuring rate: | 0.001 S |
| Temperature range: | 50 to 400°C |
| Temperature precision: | ± 0.5°C |
| Measuring range: | 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density) |
| Measuring rate: | 0.001 S |
| Temperature range: | 50 to 400°C |
| Temperature precision: | ± 0.5°C |
| Inclined adjustable angle: | 0 to 40° |
| Panel width: | 120 mm |
| Test area width: | 80 mm |
| Standard steel balls: | 1/32 to 1 inch |
| Operating temperature: | Ambient temperature to 300°C |
| Heating rate: | 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min) |
| Maximum temp. error with heating speed: | ± 5°C under 50°C/ h, ± 1°C under 120°C/ h |
| Range of deformation: | 0 to 10 mm |